JH-9610is made up of three packs: A,B and C;
Pack A: It is silver gray slurry that mainly chemically combined
with super fine flake Zn, super fine flake Al and organic additive.
Pack B: It is water solution that mainly combined with corrosion
protecion additive, particular regulator water solution etc.
Pack C: It is the tackifier of the coating which mainly made up of
cellulose white or yellowish powder.
1. Chrome free
2. Good surface finish performance,high anti-corrosion,low friction
3. No hydrogen brittleness,no pickling process.
4. Good heat resistance.
5. Good SST hours ,anti-aging cycle is long, can coat more products
under the same process conditions.
1. Mix Ratio
Pack A: Pack B: Pack C=1:1: X(according to different viscosity
2. Before Mixture, Keep weighted A&B into the water bath at
25±2℃ , then stir A to make metal slurry disperse uniformly by
frequency mixer ,after A is fully evenly dispersed, reduce the
agitating speed to 60r/min, and add B.
3. Add B to the stirring A slowly.
4. Stir the mixture about 1~2 hours after B added, then add C. C
should be powdered if lump exist.(The barrel temperature should not
be lower than 20℃, otherwise C will not be dissolved sufficiently
.)Then stir 10~12 hours alowly and continuously.
|2||Coating method||Dip and spraying|
|4||Specific gravity||1.45±0.1(Spray Coating)|
Caution: Temperature should be controlled in above operation.
1. Other chemicals such as any kinds of acid, alkali salt can not
be mixed into coating, for these can activate Zn & Al plate to
aging the coating.
2. Avoid irradiation of sunshine and ultraviolet ray for long time
when operating, otherwise it will accelerate aging or
polymerization of the coating .
3. It is very important to control the temperature of coating. If
the temperature of coating changes when operating, it will effect
the viscosity, then effec the coating quatity on workpiece. So the
relations among temperature,viscosity and spinning process shoud be
controlled well when coating.
4. The viscosity will be different if coating method is different.
Choose low data if spray coating,and choose high data if dip spin